Low alloy high strength steel EN 10025 S355JR properties
Low alloy high strength steel EN 10025 S355JR properties
Low alloy high strength steel EN 10025 S355JR is structural steel which can be readily welded to other weldable steel. With its low carbon equivalent, low alloy high strength steel EN 10025 S355JR possesses good cold-forming properties. Low alloy high strength steel EN 10025 S355JR plate is produced by fully killed steel process and supplied in normalized or controlled rolling condition.
Low alloy high strength steel EN 10025 S355JR properties - S355JR chemical composition (max %):
| Grade | C% | Si % | Mn % | P % | S % | N % | Cu % |
| S355JR | 0.27 | 0.60 | 1.70 | 0.035 | 0.035 | 0.012 | 0.60 |
Low alloy high strength steel EN 10025 S355JR properties - S355JR mechanical properties.
| Grade | Thickness (mm) | Min Yield (Mpa) | Tensile (Mpa) | Elongation (%) | Min Impact Energy | |
| S355JR | 8mm-100mm | 315Mpa-355Mpa | 450-630Mpa | 18-20% | 20 | 27J |
| 101mm-200mm | 285-295Mpa | 450-600Mpa | 18% | 20 | 27J | |
| 201mm-400mm | 275Mpa | - | 17% | 20 | 27J | |
| The min impact energy is longitudinal energy | ||||||
Low alloy high strength steel EN 10025 S355JR offers high yield and tensile strength and is supplied with a variety of treatments and test options to ensure that it is a highly usable steel in your various projects. Low alloy high strength steel EN 10025 S355JR is widely used in the structural engineering and industries.